ULTEM 9085 SPEC SHEET
ULTEM 9085 is a flame retardant high performance thermoplastic for direct digital manufacturing and rapid prototyping. It is ideal for the transportation industry due to its high strength-to-weight ratio and its FST (flame, smoke, and toxicity) rating. This unique material's preexisting certifications make it an excellent choice for the commercial transportation industry - especially aerospace, marine and ground vehicles. Combined with a Fortus® 3D Production System, ULTEM 9085 allows design and manufacturing engineers to produce fully functional parts that are ideal for advanced functional prototypes or end use without the cost or lead time of traditional tooling. | |||
Mechanical Properties | Test Method | English | Metric |
Tensile Strength, Yield (Type 1, 0.125", 0.2"/min) | ASTM D638 | 6,800 psi | 47 MPa |
Tensile Strength, ULtimate (Type 1, 0.125", 0.2"/min) | ASTM D638 | 9,950 psi | 69 MPa |
Tensile Modulus (Type 1, 0.125", 0.2"/min) | ASTM D638 | 312,000 psi | 2,150 MPa |
Tensile Elongation at Break (Type 1, 0.125", 0.2"/min) | ASTM D638 | 5.8% | 5.8% |
Tensile Elongation at Yield (Type 1, 0.125", 0.2"/min) | ASTM D638 | 2.2% | 2.2% |
Flexural Strength (Method 1, 0.05"/min) | ASTM D790 | 16,200 psi | 112 MPa |
Flexural Modulus (Method 1, 0.05"/min) | ASTM D790 | 331,000 psi | 2,300 MPa |
Flexural Strain at Break (Method 1, 0.05"/min) | ASTM D790 | No break | No break |
IZOD Impact, notched (Method A, 23°C) | ASTM D256 | 2.2 ft-lb f/in | 120 J/m |
IZOD Impact, un-notched (Method A, 23°C) | ASTM D256 | 14.6 ft-lb f/in | 781 J/m |
Compressive Strength, Yield (Method 1, 0.05"/min) | ASTM D695 | 14,500 psi | 100 MPa |
Compressive Strength, Ultimate (Method 1, 0.05"/min) | ASTM D695 | 26,200 psi | 181 MPa |
Compressive Modulus(Method 1, 0.05"/min) | ASTM D695 | 1,030,000 psi | 7,012 MPa |
All Mechanical Properties listed above are for the XZ Orientation, please see full details here |
Thermal Properties | Test Method | English | Metric |
Heat Deflection (HDT) @ 66 psi, 0.125" unannealed | --------------- | --------------- | --------------- |
Heat Deflection (HDT) @ 264 psi, 0.125" unannealed | ASTM D648 | 367°F | 186°C |
Glass Transition Temperature (Tg) | DSC (SSYS) | 367°F | 186°C |
Coefficient of Thermal Expansion | ASTM E831 | 36.7 x 10-6 in/(in·F°) | 65.27 µm/(m·C°) |
Melting Point | --------------- | Not Applicable* | Not Applicable* |
Electrical Properties | Test Method | Value Range |
Volume Resistivity | ASTM D257 | 4.9 x 1015 - 8.2 x 1015 ohms |
Dielectric Constant | ASTM D150-98 | 3 - 3.2 |
Dissipation Factor | ASTM D150-98 | .0026 - .0027 |
Dielectric Strength | ASTM D149-09, Method A | 110 - 290 V/mil |
Other Test | Method | Value |
Specific Gravity | ASTM D792 | 1.34 |
Rockwell Hardness | ASTM D785 | --- |
Flame Classification | UL94 | V-0 (1.5 mm, 3 mm) |
Oxygen Index | ASTM D2863 | 0.49 |
OSU Total Heat Release (2 min test, 0.060" thick) | FAR 25.853 | 16 kW min/m2 |
UL File Number | --------------- | E345258 |
Outgassing | ||
Total Mass Loss (TML) | ASTM E595 | 0.41% (1.00% maximum) |
Collected Volatile Condensable Material (CVCM) | ASTM E595 | -0.1% (0.10% maximum) |
Water Vapor Recovered (WVR) | ASTM E595 | -0.37% (report) |
Fungus Resistance (Method 508.6) | MIL-STD-810G | Passed |
Burn Testing | ||
Horizontal Burn (15 sec) | 14 CFR/FAR 25.853 | Passed (0.060” thick) |
Vertical Burn (60 sec) | 14 CFR/FAR 25.853 | Passed (0.060” thick) |
Vertical Burn (12 sec) | 14 CFR/FAR 25.853 | Passed (0.060” thick) |
45° Ignition | 14 CFR/FAR 25.853 | Passed (0.060” thick) |
Heat Release | 14 CFR/FAR 25.853 | Passed (0.060" thick) |
NBS Smoke Density (flaming) | ASTM F814/E662 | Passed (0.060" thick) |
NBS Smoke Density (non-flaming) | ASTM F814/E662 | Passed (0.060" thick) |
System Availability | Layer Thickness Capability | Support Structure | Available Colors |
Fortus 900mc | 0.013 inch (0.330 mm) | BASS | Tan (Natural) and Black |
0.010 inch (0.254 mm) |
*Due to amorphous nature, material does not display a melting point |